ST37 ST35 ST52 bomba la chuma la usahihi wa juu
Din 2391 bomba la chuma isiyo imefumwa (Din 2391, En 10305-1, en 10305-4, BS 6323 precision chuma imefumwa tube NBK GBK)
Vipimo
| Kawaida | DIN2391 DIN1630 DIN2448 |
| Daraja | ST35/E235 ST37.4 ST45/E255 ST52/E355 |
| Hali ya Uwasilishaji | NBK(+N) BK(+C) GBK(+A) BKW(+LC) BKS(+SR) |
| Ukubwa | OD:4 hadi 219mm Unene 0.5-35mm, Urefu: 3m, 5.8,6 au kulingana na mahitaji |
| Maliza | Uso wa mabati (Sliver/Njano/Rangi) Mipako ya zinki ya 8-12um |
| Maombi | Mfumo wa Hydraulic;Gari/basi;gari la ujenzi |
| Wakati wa utoaji | Siku A.3 ikiwa bidhaa hii ni ya hisa. B. Takriban siku 30 kulingana na wingi |
TIBA ZA USO
1. Tube Bare (Hakuna mipako): Bright na laini
A. Mabati ya fedha
B. Mabati ya manjano
C. Olive kijani coated
Unene wa safu: 8-20um, Mtihani wa Dawa ya Chumvi: masaa 48-150
3. Fosfati nyeusi
Viwanja Tofauti
1. Mashamba ya magari
A. Njia za sindano/nozzles za mafuta
B. CNG (Gesi Asilia Iliyobanwa)-- Shinikizo la kupasuka: 1307Bar, Shinikizo la Kufanya kazi: karibu 350bar
C. Usambazaji wa Hifadhi: Vipengele vya safu ya uendeshaji
D. Vishikizo vya gia, breki za mkono, ekseli za mbele, vipumulio vya mikoba ya hewa, vidhibiti, viungio vya viti, viunzi vya gurudumu la mbele.
2. Mashamba ya Hydraulic
A. Saketi za majimaji (HPL), mistari ya nyumatiki, na kusimamishwa kwa majimaji
B. Mitungi ya majimaji (HPZ)
Muundo wa Kemikali
| Daraja la chuma | C | Si | Mn | P | S | Al | |
| Jina | Hapana. | max | max | max | max | max | max |
| ST35 | 1.0308 | 0.17 | 0.35 | 0.4 (dakika) | 0.025 | 0.025 | - |
| ST45 | 1.0408 | 0.21 | 0.35 | 0.4 (dakika) | 0.025 | 0.025 | - |
| ST52 | 1.058 | 0.22 | 0.55 | 1.6 | 0.025 | 0.025 | - |
Sifa za Mitambo
| Daraja la chuma | Nguvu ya Mazao (Mpa) | Nguvu ya Mkazo (Mpa) | Kurefusha (%) | |
| Jina | Hapana. | ReH (dakika) | Rm(dakika) | A(dakika) |
| ST35 | 1.0308 | 235 | 340 hadi 480 | 25 |
| ST45 | 1.0408 | 255 | 440 hadi 570 | 21 |
| ST52 | 1.058 | 355 | 490 hadi 630 | 22 |
Uvumilivu
| OD | Uvumilivu unaoruhusiwa | Uvumilivu Maalum | ||
|
| GB/T3639 | DIN2391 | OD | WT |
| 4 mm-20 mm | ± 0.10mm | ±0.08mm | ± 0.05mm | ± 0.05mm |
| 20-30 mm | ± 0.10mm | ±0.08mm | ±0.08mm | ±0.08mm |
| 31 mm-40 mm | ± 0.15mm | ± 0.15mm | ± 0.10mm | ±0.08mm |
| 41-60 mm | ± 0.20mm | ± 0.20mm | ± 0.15mm | ± 0.15mm |
| 61mm-80mm | ± 0.30mm | ± 0.30mm | ± 0.20mm | ± 0.20mm |
| 81mm-120mm | ± 0.45mm | ± 0.45mm | ± 0.30mm | ± 0.30mm |
Hali ya Uwasilishaji
| Uteuzi | Alama | Maelezo |
| Baridi imekamilika (ngumu) | BK(+C) | Mirija haifanyi matibabu ya joto kufuatia uundaji wa baridi ya mwisho na, kwa hivyo, ina upinzani wa juu kwa deformation |
| Baridi imekamilika (Laini) | BKW | Matibabu ya mwisho ya joto hufuatiwa na kuchora baridi inayohusisha deformation ndogo.Usindikaji zaidi unaofaa huruhusu kiwango fulani cha uundaji baridi (kwa mfano, kupinda, kupanua) |
| (+LC) | ||
| Baridi imekamilika na kupunguza mkazo | BKS(+SR) | Matibabu ya joto hutumiwa kufuatia mchakato wa mwisho wa kuunda baridi.Kwa kuzingatia hali zinazofaa za usindikaji, ongezeko la mikazo ya mabaki inayohusika huwezesha kuunda na kutengeneza kwa kiwango fulani. |
| Annealed | GBK(+A) | Mchakato wa mwisho wa kuunda Baridi hufuatwa na kuingizwa kwenye angahewa iliyodhibitiwa. |
| Imesawazishwa | NBK(+N) | Mchakato wa mwisho wa uundaji wa baridi hufuatwa na kuingizwa juu ya sehemu ya juu ya mabadiliko katika anga inayodhibitiwa. |
Ubora
1. Madhubuti kulingana na DIN2391/EN10305 au kiwango kingine.
2. Sampuli: Sampuli ni bure kwa majaribio.
3. Vipimo: Mtihani wa dawa ya chumvi/Mtihani wa Kupunguza nguvu / Mtihani wa sasa wa Eddy / Mtihani wa muundo wa kemikali kulingana na ombi la wateja
4.Cheti: IATF16949, ISO9001, SGS nk.
5.EN 10204 3.1 Uthibitisho
Ufungaji wa bidhaa